Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers End Uses
- Processing Recommendations
Material needs to be dried prior processing at 175-195°F for 3 hours, preferably using a dehumidifying drier fed by air exhibiting a dew point lower than -22°F.
Suggested molding temperature profile:Zone Temperature Zone 1 375°F Zone 2 385°F Zone 3 390°F Nozzle 395°F Being affected by type of machine used, processing conditions and downstream equipment, the temperature profiles as given above has to be considered as just indicative.
Properties
- Physico-Chemical Properties
Value | Units | Test Method / Conditions | |
Tensile Strength | 8000 | psi | ASTM D412 |
Vicat Softening Point | 293 | °F | ASTM D1525 |
Tensile Modulus (at 50%) | 1200 | psi | ASTM D412 |
Tensile Modulus (at 300%) | 3100 | psi | ASTM D412 |
Tensile Modulus (at 100%) | 1500 | psi | ASTM D412 |
Tear Strength | 91 | N/mm | ASTM D624 |
Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
Shore Hardness | 92 | A Scale | ASTM D2240 |
Flexural Modulus | 6400 | N/mm² | ASTM D790 |
Compression Set (at 70h/23°C) | 16 | % | ASTM D395 |
Abrasion Loss | 30 | mm³ | DIN 53516 |
Elongation (at Break) | 500 | % | ASTM D412 |
Compression Set (at 22h/70°C) | 28 | % | ASTM D395 |
Packaging & Availability
- Regional Availability
- Packaging Information
Laripur® 2203-93A is supplied in regular pellet form and it is packaged in 25 kg bags or 500 kg and 1000 kg octabins
Storage & Handling
- Shelf Life
- 6 months
- Storage and Shelf Life Conditions
- Laripur® 2203-93A must be stored in its original and sealed containers and kept in a dry and well ventilated place; avoiding the direct sun radiation.
- The shelf life of Laripur® 2203-93A will be 6 months from the date of delivery to the final customer, when stored in its original sealed packaging and in proper conditions