Deuteron® LE 512

• Deuteron®’s antistatic additives are able to achieve resistivity ranges between 1x105 und 1*109 Ω (100 kΩ - 1 G Ω) – Anti-static properties according to EN ISO 20345.
• Anti-static shoes: 1x105 und 1*108 Ω (100 kΩ -100 MΩ) (according to EN 61340-4-3) ESD applications: 1x105 und 3,5*107 Ω (100 kΩ -35 MΩ) (according EN 61340-5-1) The effect of quaternary ammonium compounds is highly influenced by the type of system (resins, additives, pigments, etc.) and by the chosen measurement conditions.

 Fields of application include:

• Electrostatic adjustment of spray paints
• PU systems (foam, shoe soles and casting resins)
• UV and EB curable systems
• PVC
• Floor coatings
• Synergistic wetting agent for carbon blacks, graphite and carbon fibers

Dosage

• Typical addition level: 0.2 % - 5 %
• The exact quantities to be used depend on the system and must be determined individually for the intended application.

Processing

• Deuteron® LE 512 can be used to prepare an interme- diate by diluting at room temperature in suitable polar solvents or water. Direct processing is only possible after melting. The melting temperature should be in a range of 95 °C - 110 °C and to ensure proper distribution the molten product should be added while stirring.

• Deuteron®’s antistatic additives are able to achieve resistivity ranges between 1x105 und 1*109 Ω (100 kΩ - 1 G Ω) – Anti-static properties according to EN ISO 20345.
• Anti-static shoes: 1x105 und 1*108 Ω (100 kΩ -100 MΩ) (according to EN 61340-4-3) ESD applications: 1x105 und 3,5*107 Ω (100 kΩ -35 MΩ) (according EN 61340-5-1) The effect of quaternary ammonium compounds is highly influenced by the type of system (resins, additives, pigments, etc.) and by the chosen measurement conditions.

 Fields of application include:

• Electrostatic adjustment of spray paints
• PU systems (foam, shoe soles and casting resins)
• UV and EB curable systems
• PVC
• Floor coatings
• Synergistic wetting agent for carbon blacks, graphite and carbon fibres

Dosage

• Typical addition level: 0.2 % - 5 %
• The exact quantities to be used depend on the system and must be determined individually for the intended application.

Processing

• Deuteron® LE 512 can be used to prepare an interme- diate by diluting at room temperature in suitable polar solvents or water. Direct processing is only possible after melting. The melting temperature should be in a range of 95 °C - 110 °C and to ensure proper distribution the molten product should be added while stirring.

• Steel drum (25 kg net)

• 24 months in tightly closed original containers at room temperature.
• At low temperatures a viscosity increase or solidification can occur. The product can be regenerated by applying gentle heat. The temperature should not exceed 40 °C.